Synthésis, characterization and photochemical durability of polymeric systems for holographic recording
Synthèse, caractérisation et durabilité de systèmes photostructurables destinés à l'holographie
Résumé
The purpose of this study is to obtain new polymeric materials for holographic recording. The first part of this work has been firstly devoted to the radical synthesis of carbazolic copolymers based of carbazolylmethacylate units spaced by octylmethacrylate groups, secondly to their purification and lastly to their characterization. An analysis of the photochemical behaviour was carried out at wavelengths above 300 nm representing the natural aging. A study of the photochemical mechanism occurring under irradiation at 405 nm (wavelength used for holographic recording) was then performed with copolymers doped with iodoform. Finally, the feasibility of holographic recording has been demonstrated using laser recording at 480 and 532 nm. Copolymers were then doped with trinitrofluorenone.
Le but de cette étude est d'obtenir de nouveaux matériaux polymères photostucturables pour l'enregistrement holographique. La première partie de ce travail a été consacrée à la synthèse radicalaire de copolymères carbazoliques à base d'unités carbazolylméthacylates espacées par des groupements octylméthacrylates, puis à leur purification et enfin à leur caractérisation. Une analyse approfondie de leur comportement photochimique a été menée à des longueurs d'onde d'irradiation supérieures à 300 nm représentatives du vieillissement naturel. Une étude des mécanismes photochimiques mis en jeu sous irradiation laser à 405 nm (longueur d'onde utilisée pour l'enregistrement holographique) a ensuite été réalisée avec des copolymères dopés avec de l'iodoforme. Enfin, la faisabilité des enregistrements holographiques a pu être démontrée sous irradiation laser à 480 et 532 nm en dopant les copolymères avec de la trinitrofluorénone
Loading...